| 日本神钢KOBELCO焊接材料 |
|
| 日期：2007-7-14 20:12:56 人气：105 [大 中 小] |
|
|
|
CM-9CBE9016-G0.061.510.319.110.94Mo:1.06Nb:0.03V:0.18600750260℃/140用于焊接工作温度在600-650的Cr9MoNiV(如T91、P91)耐热钢，如蒸汽管道和过热器管等。 TIG焊丝 类别品名AWS型号熔敷金属化学成分(%)熔敷金属力学性能保护气体简明与用途CMnSiCrNi其它σ0.2
(MPa) δb
(MPa) δ
(%) IV
(J) T
I
G
焊
丝TGS-1CMER80S-G0.060.990.501.22-Mo:0.54540630280℃/Ar焊接1-1.25%Cr-0.5Mo耐热钢。TGS-1CMLER80S-G0.021.100.481.38-Mo:0.5048058031℃/Ar同TGS-1CM，但因含碳量低，抗裂性优良。TGS-2CMER90S-G0.090.710.322.26-Mo:1.0461072028℃/Ar焊接2.25%Cr-1%Mo耐热钢。TGS-2CMLER80S-G0.031.090.492.22-Mo:1.0152063028℃/Ar同TGS-2CM，但因含碳量低，抗裂性优良。TGS-5CMER80S-B60.080.490.285.13-Mo:0.0648060026℃/Ar焊接5%Cr-0.5%Mo耐热钢。TGS-9CMER80S-B80.060.560.258.70-Mo:1.0941059032℃/Ar焊接9%Cr-1%Mo耐热钢。TGS-9CbER90S-G0.070.990.168.970.68Mo0.9
Nb0.04V0.1870078024℃/Ar焊接9%Cr-1%Mo-Nb-V耐热钢。TGS-709S-0.020.030.032.070.4Mo19.0
W3.0Fe5.546073047℃/Ar属70%Ni-18%Mo-Cr-W哈斯特洛依系，焊9%Ni低温钢。
药芯焊丝 类别品名AWS型号熔敷金属化学成分(%)熔敷金属力学性能特性与用途CMnSiCrNi其它σ0.2
(MPa) δb
(MPa) δ
(%) IV
(J) 药
芯
焊
丝DW-100E71T-10.051.350.45--510570300℃/110钛型渣系CO2焊接，用于船舶，桥梁，贮罐等结构。MX-100E71T-10.061.350.62--510580300℃/88金属粉芯焊丝CO2焊接，用于建筑机械，钢架等。MX-100TE71T-1/-1M0.081.530.49--480560310℃/98薄板焊接用CO2/Ar+CO2焊接，用于汽车，车辆及管道焊接。OW-56E70T4-K20.080.940.09--420550280℃/98自保护焊丝，特别适用于中，厚板结构的室外焊接。OW-56AE70T-40。090。870。15410570280℃/29自保护焊丝，用于焊接土木建筑（PC桩，钢管桩）钢架的室外焊接。DW-60E81T1-Ni10.051.130.33-1.00Mo:0.2156062027-20℃/100钛型渣系CO2焊接，焊接60kgf级高强度钢结构。DWS-43GEG70T-20.081.630.35--Mo:0.1747060027-20℃/62细丝CO2保护气电立焊用，焊接船舶外壳，贮罐侧板等。HS-42G-0.071.780.38--Mo:0.1345059027-20℃/59粗丝CO2保护气电立焊用，焊接船舶外壳，纵隔板等。DWS-60G-0.081.580.41-0.51Mo:0.3252065024-20℃/59细丝CO2保护气电立焊用，焊接60kgf级高强度钢结构。 MIG焊丝 类别品名AWS型号熔敷金属化学成分(%)熔敷金属力学性能保护气体简明与用途CMnSiCrNi其它σ0.2
(MPa) δb
(MPa) δ
(%) IV
(J) M
I
G
焊
丝MG-1CMER80S-G0.071.06 0.561.32-Mo:0.57510630230℃/88CO21~1.25%Cr-0.5%Mo耐热钢CO2焊接用。MGS-1CMER90S-G0.101.220.322.31-Mo:1.01580690230℃/78CO22.25%Cr-1%Mo耐热钢CO2焊接用。MGS-1CMER80S-G0.070.740.341.23-Mo:0.52570680220℃/69Ar+2-5%O2
100% CO21~1.25%Cr-0.5%Mo耐热钢，短路电弧焊接用MGT-1CMER80S-G0.050.680.451.27-Mo:0.54460580270℃/140Ar+2%O2
100% CO21~1.25%Cr-0.5%Mo耐热钢，短路电弧焊接用MGT-2CMER90S-G0.080.760.342.29-Mo:0.98550670260℃/110Ar+2-5%O2或
Ar+5-20%CO22。25~1%Mo耐热钢，喷射电弧焊接用MGT-2CMER90S-G0.070.750.432.31-Mo:0.99550680230℃/130Ar+2%O2
100%CO2 2.25~1%Mo耐热钢，短路电弧焊接用MGS-5CMER80s-B60.080.560.295.46-Mo:0.53480640260℃/78Ar+2-5%O2或
Ar+5-20%CO2 5%Cr-0.5%Mo耐热钢，喷射电弧焊接用MGS-9CMER80S-B80.080.490.389.01-Mo:1.04480640240℃/130Ar+2-5%O2或Ar+5-20CO29%Cr-1%Mo耐热钢，喷射电弧焊接用MGS-9CbER90S-G0.081.290.278.860.38Mo0.98
Nb0.03V0.19480640240℃/98Ar+5%CO29%Cr-1%Mo-Nb-V耐热钢，喷射电弧焊接用 |
|
|